X6CrNi18-11
| Product parameters | |
| Material Category:: | Superalloy |
| Steel Grade: | X6CrNi18-11 |
| Material Technical Standards:: | DIN |
| Specification Code:: | DIN 17742, 17460, 17480 (2002/1992), DIN EN 103021, 10296, 10095 (2002/1999) |
| Place of Origin: | Germany |
Description
Introduction:
X6CrNi18-11 usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
X6CrNi18-11 usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition.
Applications:
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.X6CrNi18-11 used for components such as
fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
All Grades Comparison
Commonly used in industries such as offshore, marine, food, paper mills, oil field and aerospace.X6CrNi18-11 used for components such as
fasteners, couplings, screws, bushings, studs, fittings, valve stems, roller, wear rings.
| DIN | W-Nr | Other |
|---|---|---|
| X6CrNi18-11 | W-Nr 1.4948 | - |
Chemical Composition (Weight %)
| C | Si | Mn | P | S | Cr | Ni | Mo | Other |
|---|---|---|---|---|---|---|---|---|
| 0.04 ～ 0.08 | ≤ 0.75 | ≤ 2.00 | ≤ 0.035 | ≤ 0.015 | 17.0 ～ 19.0 | 10.0 ～ 12.0 | - | N ≤ 0.11 |
| Condition of heat treatment | Tensile Rm(MPa) |
Yield Rp0.2(MPa) |
Elongation A(%) |
Reduction in cross section on fracture Z (%) |
Impact AKV/AKU(J) |
Brinell Hardness(HBW) |
|---|---|---|---|---|---|---|
| Annealing | - | - | - | - | - | - |
| Q/T | 490 ～ 690 | ≥ 185 | ≥ 40.0 | - | ≥ 85 | - |
Round bar (Diameter): 5.5 mm to 700 mm
Wire rod (Diameter): 0.10 ~ 16mm
Square bar / Flat bar: 5mm to 550mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forged ring: OD200 ~ 1500mm X ID150 ~ 1250mm X H20 ~ 1250mm
Heavy/middle plate via hot rolled: T50 - 200mm X W80- 1200mm X L1000-3000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Length: Fixed length or random length or based on the customer's special requirement.