X5CrNiCu17-4 Precipitation Hardening Steel
Specifications Ex-stock X5CrNiCu17-4 Datasheet, X5CrNiCu17-4 Chemical Flat Bar Forging Ex-stock & Plate Heat treatment Machined, Rod Exporters Ex-stock Sale - Technical standards.
| Product parameters | |
| Material Category:: | Martensitic PH Stainelss Steel |
| Stocklist & Inventory Available:: | Round bar Diameter ranges from 15 to 300mm in Stock |
| Product Shapes:: | Round bar / Flat bar |
| Heat Treatment Practice:: | Solution annealed 1040 ℃, water, oil or air cooled, aged 480 / 550 / 580 / 620 ℃, air cooled |
| Ultrasonic Test Standard:: | ASTM E2375 / MIL-STD- AMS 2154 / SEP 1923 / GB/T 4162 / EN 10228-3 / EN 10308 |
| Standard Export Packing Way:: | Wooden box, pallet / tray free from fumigation |
| Unit price: | USD6.95 per kg / Negotiable |
| Production Lead Time:: | Within 35 days after 40% deposit prepayable |
Description
Technical Datasheet - DIN X5CrNiCu17-4
Material type: Precipitation hardening corrosion resisting steels
Material specifications: DIN 17445,17440, DIN EN 10088-1, 10297,10272,10312, DIN EN 10088-5(2005)
Typical Applications
Grade X5CrNiCu17-4, it is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc.
Medical equipment, Chemical equipments.
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts, Pressure vessel.
Profile and dimensions:
Round bar / Wire rod (Diameter): 5.5 to 650mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W50 - 1200mm X L1000 - 5000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Chemcial Compositions (Mass weight %)
C (％): ≤ 0.07, Si (％): ≤ 0.70, Mn (％): ≤ 1.50, P (％)≤: 0.040, S (％)≤: 0.030
Cr (％): 15.0 ～ 17.0, Ni (％): 3.00 ～ 5.00, Mo (％): -, Cu (％): 3.00～5.00
Nb (%): 5 × C％ ~ 0.45, Fe (%): Balance
Mechanical Properties under Room Temperature.
Condition: hardening
Thickness/mm: 100
Tensile strength, σb/MPa: 1070 ~ 1270
Yield strength, σ0.2≥/MPa: 1000
Elongation, δ5 ≥(％): 10
Reduction of area, ψ≥ (％): -
Akv≥/J: -
Hardness HBS30: -