X5CrNiMo16-5
Description X5CrNiMo16-5 datasheet, X5CrNiMo16-5 Chemical, X5CrNiMo16-5 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials c
| Product parameters | |
| Material Category:: | Stainless Steel |
| Steel Grade: | X5CrNiMo16-5 |
| Material Technical Standards:: | DIN |
| Specification Code:: | DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312 |
| Place of Origin: | Germany |
Description
MARTENSITIC STAINLESS DATASHEET - DIN X5CrNiMo16-5
MATERIAL CATEGORY - Martensitic precipitation hardening corrosion resisting steels
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.06
Si (％): ≤ 0.70
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 4.00 ~ 6.00
Mo (％): 0.80 ~ 1.50
N (％): ≥ 0.020
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: annealed
Thickness/mm: -
Tensile strength, σb/MPa: 1100max.
Yield stength, σ0.2≥/MPa: -
Elongation, δ5≥(％): -
Reduction of Area, ψ ≥(％): -
Impact, Akv≥/J: -
Hardness HBS30: 320max.
Condition: Quenched and tempered T900
Thickness/mm: 160~25
Tensile strength, Rm,σb/MPa: 900 ~ 1100
Yield strength, Re, σ0.2≥/MPa: 700
Elongation, δ5≥(％): 14.0
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: 80/60
Hardness HBS30: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 ~ 1000mm X L1000 ~ 4000mm
Sheet steel via cold rolled: T1.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.50 ~ 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@cnlhss.com) our resident team of qualified production engineers.
MATERIAL CATEGORY - Martensitic precipitation hardening corrosion resisting steels
MATERIAL SPECIFICATIONS - DIN 17445,17440(1999/1996), DIN EN 10088-1, 10297,10272,10312
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.06
Si (％): ≤ 0.70
Mn (％): ≤ 1.50
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 4.00 ~ 6.00
Mo (％): 0.80 ~ 1.50
N (％): ≥ 0.020
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Condition: annealed
Thickness/mm: -
Tensile strength, σb/MPa: 1100max.
Yield stength, σ0.2≥/MPa: -
Elongation, δ5≥(％): -
Reduction of Area, ψ ≥(％): -
Impact, Akv≥/J: -
Hardness HBS30: 320max.
Condition: Quenched and tempered T900
Thickness/mm: 160~25
Tensile strength, Rm,σb/MPa: 900 ~ 1100
Yield strength, Re, σ0.2≥/MPa: 700
Elongation, δ5≥(％): 14.0
Reduction of area, ψ≥(％): -
Impact strength, Akv≥/J: 80/60
Hardness HBS30: -
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Medical equipment
Chemical equipments
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
PRODUCT PROFILE & FORMS
Round bar / Wire rod (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W100 ~ 1000mm X L1000 ~ 4000mm
Sheet steel via cold rolled: T1.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.50 ~ 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.