AISI 316 / S31600 Corrosion-Resisting Steel
| Product parameters | |
| Material Category:: | Austenitic Stainless Steel |
| Material Technical Standards:: | ASTM A276 |
| Place of Origin: | P.R. China |
| Stocklist & Inventory Available:: | Diameter 15 ~ 230mm |
| Melting Process Route:: | EAF + VD + LF / BEF + AOD / +ESR |
| Min. order quantity Per Batch:: | 500 kg |
| Production Lead Time:: | Within 15 days after 40% deposit in advance. |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
Technical Data Sheet
The alloy is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition. Forms and Shapes:
Round bar (Diameter): 5.50 ~ 650mm
Square bar / Flat bar: 3 ~ 650mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the annealed condition. Forms and Shapes:
Round bar (Diameter): 5.50 ~ 650mm
Square bar / Flat bar: 3 ~ 650mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM
| C (％) | ≤ 0.08 |
| Si(％) | ≤ 1.00 |
| Mn(％) | ≤ 2.00 |
| P(％) | ≤ 0.045 |
| S (％) | ≤ 0.030 |
| Cr (％) | 16.0 ～ 18.0 |
| Ni (％) | 10.0 ～ 14.0 |
| Mo(％) | 2.00 ～ 3.00 |
| Other (％) | - |
| Condition of heat treatment | - |
| Tensile Rm (MPa) | 515 |
| Yield Rp0.2 (MPa) | 205 |
| Elongation A (%) | 40 |
| Reduction in cross section on fracture Z (%) | 50 |
| Impact AKV/AKU (J) | - |
| Brinell Hardness (HBW) | 217 max |