UNS S31600 / AMS 5648 ESR Remelted Stainless Steel
| Product parameters | |
| Material Category:: | Austenitic Stainless Steel |
| Material Technical Standards:: | ASTM A276 / AMS 5648L |
| Place of Origin: | P.R. China |
| Stocklist & Inventory Available:: | Diameter 15 ~ 230mm |
| Melting Process Route:: | EAF + VD + LF / BEF + AOD / +ESR |
| Min. order quantity Per Batch:: | 500 KG |
| Certification:: | MTR, COC, Certificate of origin, Form A/E, Invoice, Packing list |
| Product Shapes:: | Round bars, flat bars, forgings, ring |
| Heat Treatment Practice:: | Solution annealed 1050 ℃, water or air cooled |
| Production Lead Time:: | Within 15 days after 40% deposit prepayable |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
Technical Data Sheet of AMS 5648 / S31600
The alloy is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the solution annealed condition.
Shapes And Dimensions:
Round bar (Diameter): 5.50 ~ 650mm
Square bar / Flat bar: 3 ~ 650mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Bars are usually supplied black/bright in the solution annealed condition.
Shapes And Dimensions:
Round bar (Diameter): 5.50 ~ 650mm
Square bar / Flat bar: 3 ~ 650mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM
| C (％) | ≤ 0.08 |
| Si(％) | ≤ 1.00 |
| Mn(％) | ≤ 2.00 |
| P(％) | ≤ 0.045 |
| S (％) | ≤ 0.030 |
| Cr (％) | 16.0 ～ 18.0 |
| Ni (％) | 10.0 ～ 14.0 |
| Mo(％) | 2.00 ～ 3.00 |
| Other (％) | - |
| Condition of heat treatment | - |
| Tensile Rm (MPa) | 515 |
| Yield Rp0.2 (MPa) | 205 |
| Elongation A (%) | 40 |
| Reduction in cross section on fracture Z (%) | 50 |
| Impact AKV/AKU (J) | - |
| Brinell Hardness (HBW) | 217 max |