1.2731 Round bar Stock Available
| Product parameters | |
| Material Category:: | Alloy 13.0Cr - 13.0Ni-2.0W Hot Working Tool Steel |
| Material Technical Standards:: | EN ISO 4957 |
| Terms of Price:: | Ex works, CIF, and CFR |
| Stocklist & Inventory Available:: | Round bar Diam. 20 ~ 200mm, and ESR Ingot |
| Melting Process Route:: | BEF + VD + ESR |
| Min. order quantity Per Batch:: | 200 KG |
| Customs HS code:: | 72222000 / 72223000 |
| Production Lead Time:: | Within 15 days after 30% downpayment. |
| Company ISO Register No:: | UQ211218R0 |
Description
RAW MATERIAL DATASHEET - W-Nr 1.2731
STOCK AVAILABLE ON HAND - ESR ingot, Round bar Diam. 20 ~ 200mm
Material Category - Hot working tool steel
Material Specifications - EN ISO 4957: 2000 , DIN 17350 (1980)
Main Chemical Elements (mass weight - %)
Carbon, C (％): 0.45 ~ 0.55
Silicon, Si (％): 1.20 ~ 1.50
Manganese, Mn (％): 0.60 ~ 0.80
Phoshorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.035
Chromium, Cr (％): 12.0 ~ 14.0
Molybdenum, Mo (％): -
Vanadium, V (％): 0.30 ~ 1.00
Nickel, Ni (％): 12.5 ~ 13.5
Tungsten, W (%): 1.50 ~ 2.80
MECHANICAL PROPERTIES & HEAT TREATMENT
Hot working tenperature ℃: 1050～850
Annealing temperature ℃: -
Hardness after annealing ≤HBW: -
Quenching temperature ℃: 980~1030
Cooling medium: Oil
Common tempering temperature ℃: 400 ~ 600
PRODUCT PROFILE & DIMENSION
Round bar / Disc (diameter1): 5.5mm to 700mm
Square bar / Flat bar: 10mm to 600mm
Forging piece: stepped shafts, other different shapes based on OEM.
STOCK AVAILABLE ON HAND - ESR ingot, Round bar Diam. 20 ~ 200mm
Material Category - Hot working tool steel
Material Specifications - EN ISO 4957: 2000 , DIN 17350 (1980)
Main Chemical Elements (mass weight - %)
Carbon, C (％): 0.45 ~ 0.55
Silicon, Si (％): 1.20 ~ 1.50
Manganese, Mn (％): 0.60 ~ 0.80
Phoshorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.035
Chromium, Cr (％): 12.0 ~ 14.0
Molybdenum, Mo (％): -
Vanadium, V (％): 0.30 ~ 1.00
Nickel, Ni (％): 12.5 ~ 13.5
Tungsten, W (%): 1.50 ~ 2.80
MECHANICAL PROPERTIES & HEAT TREATMENT
Hot working tenperature ℃: 1050～850
Annealing temperature ℃: -
Hardness after annealing ≤HBW: -
Quenching temperature ℃: 980~1030
Cooling medium: Oil
Common tempering temperature ℃: 400 ~ 600
PRODUCT PROFILE & DIMENSION
Round bar / Disc (diameter1): 5.5mm to 700mm
Square bar / Flat bar: 10mm to 600mm
Forging piece: stepped shafts, other different shapes based on OEM.