W-Nr 1.2714 / 55NiCrMoV7 Hot Work Tool Steel
| Product parameters | |
| Material Category:: | Cr-Ni-Mo-V hot work tool steel |
| Material Technical Standards:: | EN ISO 4957 - 2000, DIN 17350 (1980). |
| Place of Origin: | P. R. China |
| Terms of Price:: | Ex works, CIF, and CFR |
| Stocklist & Inventory Available:: | Round bar Diam. 90 ~ 400mm, Hot forged heavy plate. |
| Melting Process Route:: | EAF + LF + VD / + ESR, BEF + ESR |
| Min. order quantity Per Batch:: | 3000 KG |
| Certification:: | Commercial Invoice, Packing list, CO, Bill of lading, Origin of Certificate, Form E |
| Surface Condition:: | Peeled - Rough turned - Shot blasted - Bright surface. |
| Ultrasonic Test Standard:: | / GB/T 4162 / EN 10228-3 / EN 10308. |
| Standard Export Packing Way:: | Wooden box, wooden Pallet / tray with free from fumigation. |
| Production Lead Time:: | Within 15 days after 30% downpayment. |
| Unified Social Credit Code:: | 91510871777942750J |
| Company ISO Register No:: | UQ211218R0 |
Description
This alloy is generally smelt in electric arc furnace EAF + VD, LF + Electroslag remelting (ESR). For a purpose of higher quality, it should be smelt via technology of vacuum refining and external refining.
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements, and further to manufacture the piston, valve, valve seat of fuel pump. Cutting tools, Mechanical parts, Air hammer tools, Piercing tools.
MATERIAL CATEGORY: Hot working tool steel
MATERIAL SPECIFICATIONS: EN ISO 4957: 2000 , DIN 17350 (1980)
CHEMICAL COMPOSITION (Mass weight %)
C (％): 0.50 ~ 0.60, Si (％): 0.10 ~ 0.40, Mn (％): 0.65 ~ 0.95
P (％)≤: 0.030, S (％)≤: 0.030
Cr (％): 1.00 ~ 1.20, Mo (％): 0.45 ~ 0.55, V (％): 0.07 ~ 0.12
Ni (％): 1.50 ~ 1.80, Fe (%): remainder.
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT
Hot working tenperature ℃: 1050～850
Annealing temperature ℃: 680~710
Hardness after annealing ≤HBW: 248
Quenching temperature ℃: 840~860
Cooling medium: air
Common tempering temperature ℃: 490~510
Hardening value after tempering at temperature /MPa |400℃: HRC51
HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
PRODUCT FORMS & DIMENSIONS
Round bar / wire rod (Diameter1): 5.5mm to 500mm
Square bar / flat bar: 10mm to 610mm
Heavy/middle plate via hot rolled: T60 - 500mm X W60 ~ 1000mm X L1000~4000mm
Sheet steel via cold rolled: T1.5 - 4mm X W100- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.5 - 3mm X W5 - 200mm X L (or in coil form)